| 2683 |
12:30 PM | Cyclic Fatigue Test of Nickel-Titanium Endodontic Instruments
R. BEER1, J. EGGERATH2, and P. GAENGLER2, 1University of Witten-Herdecke, Faculty of Dental Medicine, Germany, 2University of Witten-Herdecke, School of Dental Medicine, Germany |
| 2684 |
12:45 PM | Fracture Behavior of NiTi Rotary Endodontic Insturments
T.A. KARN1, J.R. KELLY1, F.C. EICHMILLER2, and L.S.W. SPANGBERG1, 1University of Connecticut, Farmington, USA, 2American Dental Association Foundation, Gaithersburg, MD, USA |
| 2685 |
1:00 PM | Fatigue of Two Pd–Ag Alloys and SEM of Fracture Surfaces
D. LI, N. BABA, S. ALAPATI, R. HESHMATI, and W.A. BRANTLEY, Ohio State University College of Dentistry, Columbus, USA |
| 2686 |
1:15 PM | SEM Observations of RaCe Rotary Instruments after Simulated Clinical Use
Y. SANLI1, S.B. ALAPATI1, J.M. NUSSTEIN1, W.A. BRANTLEY1, N. BABA1, T. SVEC2, and J.M. POWERS2, 1Ohio State University, Columbus, USA, 2University of Texas Health Science Center at Houston Dental Branch, USA |
| 2687 |
1:30 PM | Nickel concentration in apically extruded debris using endodontic rotary-systems
F. PAQUÉ1, U. MUSCH1, K. BECKER2, and T. ATTIN2, 1University of Zürich, Switzerland, 2University of Göttingen, Germany |
| 2688 |
1:45 PM | Comparison of Bending Properties of Three Brands of Beta-Titanium Wires
A.B. WADE, W.A. BRANTLEY, R.G. RASHID, and S. SHANKER, The Ohio State University College of Dentistry, Columbus, USA |
| 2689 |
2:00 PM | Frictional Forces in Carbon-coated Orthodontic Wires and Brackets
S.S. KHAJOTIA, G.S. COOPER, R.S. NANDA, and G.F. CURRIER, University of Oklahoma, College of Dentistry, Oklahoma City, USA |
| 2690 |
2:15 PM | XRD Study of Low-Temperature Phase Transformations in Nickel-Titanium Orthodontic Wires
M. IIJIMA1, W.A. BRANTLEY2, Y. YONEKURA1, T. YUASA1, H. OHNO1, and I. MIZOGUCHI1, 1Health Sciences University of Hokkaido, Japan, 2The Ohio State University, Columbus, USA |
|